Propafilm™ RGR02/120
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v7pyVG_Propafilm-RGR02-120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
One Side Treated Release Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with surface polymers. RGR02/60 &120 are particularly suited for tape and release applications, in which RGR02 could be reverse printed and laminated to another web. ROR02/60 is suited for the outer web of foil laminations used in condiment sachet applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow (129°C, 1 min) | 6.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3000 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 2490 | MPa | |
| 1% Secant, TD | 2090 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 230 | MPa | |
| TD : Yield | 190 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 90 | % | |
| TD : Break | 130 | % | |
| Oxygen Permeability (23°C, 0% RH) | 41 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 5.0 | g/m²/24 hr | ASTM F1770 |
| Corona Treatment | 38 | dyne/cm | Internal Method |
| Yield | 36.7 | m²/kg | Internal Method |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen COAT EP/60 BIANCO | LyondellBasell Industries | PP Copolymer | Moplen |
| Cariflex® IR0401 BU | Kraton Polymers LLC | IR | Cariflex® |
| FHR Polypropylene AP6835-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| INEOS PP 200-CA02 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| LNP™ FARADEX™ AS002 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |