Marlex® HMN TR-938 is a Medium Density Polyethylene material. It is available in Latin America or North America for rotational molding. Important attributes of Marlex® HMN TR-938 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693A | ||
| 10% Igepal, Compression Molded, F50 | 200 | hr | |
| 100% Igepal, Compression Molded, F50 | > 1000 | hr | |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.17 mm, Rotational Molded) | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.17 mm, Rotational Molded) | 700 | % | ASTM D638 |
| Flexural Modulus 3 | ASTM D790 | ||
| 2% Secant : 3.17 mm, Rotational Molded | 660 | MPa | |
| Tangent : 3.17 mm, Rotational Molded | 820 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact | |||
| -40°C, 3.20 mm | 95.0 | J | |
| -40°C, 6.35 mm | 237 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.17 mm, Rotational Molded | 62.0 | °C | |
| 1.8 MPa, Unannealed, 3.17 mm, Rotational Molded | 42.0 | °C | |
| Brittleness Temperature | -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 117 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 128 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roechling SUSTAABS | Röchling Sustaplast SE & Co. KG | ABS | Roechling |
| RTP 2700 S-30A MD NATURAL | RTP Company | SEBS | RTP |
| XYRON™ EV103 | Asahi Kasei Chemicals Corporation | PPE+PP | XYRON™ |
| Pemex PX 20020 X | Pemex Petroquímica | LDPE | Pemex |
| SQUARE® LSR3910-40/CA2801 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |