Infino HF-1023IM
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v5aUHv_InfinoHF1023IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HF-1023IM is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. The main features are: Rohs certification. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.44 - 0.53 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.45 - 0.55 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.45 - 0.55 | % | ISO 2577 |
| Traffic : 3.20mm | 0.44 - 0.53 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C) | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 59.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 69.0 | MPa | ASTM D638 |
| Fracture | 96.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 120 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 83.0 | MPa | ASTM D790 |
| -- 8 | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 68 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 690 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 540 | J/m | ASTM D256 |
| 23°C 10 | 63 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 133 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 130 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 126 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 120 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P8-32FG-2610 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| 4MID® 9A22130 H | 4Plas | Nylon 66 | 4MID® |
| Kumho SAN SAN 335T | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| Grilamid® XE 4074 nat | EMS-GRIVORY | Nylon 612 | Grilamid® |
| SQUARE® LFR1971-60A/B | Shenzhen SQUARE Silicone Co., Ltd. | Fluoro Si | SQUARE® |