MEGOLON™ HF 8110
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v5LOeg_MEGOLON-HF-8110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MEGOLON HF8110 is a thermoplastic, halogen free, fire retardant compound for use as low voltage insulation or sheathing/jacketing. Suitable for thin wall applications. Good processability on low compression screws. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 33 | g/10 min | ISO 1133 |
| Mooney Viscosity (ML 1+4, 140°C) | 40 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 1 | 12.4 | MPa | IEC 60811-1-2 |
| -- | 11.5 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Break 2 | 130 | % | IEC 60811-1-2 |
| Break | 160 | % | IEC 60811-1-1 |
| Elongation at Break - after 4 hours, in ASTM #2 Oil (70°C) | 180 | % | |
| Tensile Strength - after 4 hours, in ASTM #2 Oil (70°C) | 8.30 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test (80°C) | 30 | % | IEC 60811-3-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission Conductivity | 0.630 | µS/cm | IEC 60754-2 |
| Acid Gas Emission pH | 4.91 | IEC 60754-2 | |
| Flammability Temperature Index | 280 | °C | ISO 4589-3 |
| Smoke Density | ASTM E662 | ||
| Flaming mode 3 | < 87 | Ds | |
| Non-flaming mode 4 | < 190 | Ds | |
| Toxicity | 2.00 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | 0.0 | % | IEC 60754-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | 8.0 | % | |
| Change in Tensile Strain at Break in Air (100°C, 168 hr) | -20 | % | |
| Change in Tensile Stress (70°C, 4 hr, in ASTM #2 Oil) | -28 | % | |
| Change in Tensile Strain at Break (70°C, 4 hr, in ASTM #2 Oil) | 15 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 34 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | after 7 days at 100°C |
| 2 . | after 7 days at 100°C |
| 3 . | Time to maximum: 10 minutes |
| 4 . | Time to maximum: 14 minutes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2307FB | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Trademark PP PPH140E | Trademark Plastics Corporation | PP Homopolymer | Trademark PP |
| TRIMID® N6-G13L | Polymer Technology and Services, LLC | Nylon 6 | TRIMID® |
| XYRON™ L565V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Flexalloy® 9600-72 | Teknor Apex Company | PVC Elastomer | Flexalloy® |