EXTEM™ XH1015 resin
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | EXTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v3Utur_EXTEM-XH1015-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyimide Extem* XH1015 Resin. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 0.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 to 1.2 | % | Internal Method |
| Water Absorption | |||
| 23°C, 24 hr 1 | 0.60 | % | ASTM D570 |
| Saturation, 23°C | 2.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3420 | MPa | ASTM D638 |
| -- | 3100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 103 | MPa | ASTM D638 |
| Yield | 101 | MPa | ISO 527-2/5 |
| Break 4 | 96.0 | MPa | ASTM D638 |
| Break | 74.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 6 | 10 | % | ASTM D638 |
| Break | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 3130 | MPa | ASTM D790 |
| -- 8 | 2870 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 120 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 168 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 10 | 4.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 250 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 235 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 237 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 224 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 260 | °C | ASTM D1525 12 |
| -- | 250 | °C | ISO 306/B50 |
| -- | 248 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 5.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 175 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Rear Temperature | 360 to 385 | °C | |
| Middle Temperature | 370 to 400 | °C | |
| Front Temperature | 380 to 410 | °C | |
| Nozzle Temperature | 375 to 405 | °C | |
| Processing (Melt) Temp | 380 to 410 | °C | |
| Mold Temperature | 150 to 175 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 70 to 100 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Results measured at 48 hrs |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC30P100-01UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| ShinkoLite-A S | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-A |
| ExxonMobil™ LDPE LD 251 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Ecomass® 1850ZC84 | Ecomass Technologies | Nylon 6 | Ecomass® |
| Jiangsu Sinarise EX9024X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |