Menzolit® SMC 1100
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v2NuBh_Menzolit-SMC-1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 1100 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor heavy metals. Menzolit® SMC 1100 is a special vinylester SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific resin and a higher amount of glass fibers results in high mechanical strength. Durability is improved as well. Even without a specific fire retardant, the fire retardancy level HB according UL 94 is achieved. Typical applictions are structural components within the automotive industry or mechanical engineering. It is suitable for load carrying applications or fast moving and accelerated components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.040 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 1.6 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 13000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 280 | MPa | ISO 178 |
| Compressive Stress | 120 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | Internal Method | |
| Matrix Crazing Strain | 0.60 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 130 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 170 | °C | Internal Method |
| Glass Transition Temperature | 162 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 160 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-50A | RTP Company | TPV | RTP |
| Sindustris ABS LHI232U | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Westlake LDPE EM811AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| UBESTA 3035 UF | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| ULTEM™ ATX200F resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |