Toughblend® PP-1600
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Toughblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v1xFuG_Toughblend-PP-1600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughblend® PP-1600 is a glass fiber reinforced coupled polypropylene compound. It's offering excellent stiffness and processability and impact resistance over a wide temperature range. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5450 | MPa | ASTM D790 |
| Flexural Strength | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 165 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 133 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2807 | NOVA Chemicals | HDPE | SCLAIR® |
| Taitacell EPS 301T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Viton® B-910 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| NYCOA Polyamide 7550 Nat | Nycoa (Nylon Corporation of America) | Nylon 12 | NYCOA Polyamide |
| Electrafil® J-1200/CF/40 NAT | Techmer Engineered Solutions | ABS | Electrafil® |