Staramide ACF2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v1rrcg_Staramide-ACF2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide ACF2 is a 10 % Carbon Fiber Reinforced Polyamide 66 injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7500 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | 1.0E+7 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6 GC | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| AKROLOY® PA CF 40 black (3639) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| K-vinyl 125 Deg C Rating Insulation (Auto) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Lumiloy® TX5300 | LG Chem Ltd. | PPE+PS+Nylon | Lumiloy® |
| PermaStat® 303 | RTP Company | PC | PermaStat® |