Durethan® BC 304 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v1lbrg_DurethanBC304000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA 6, non-reinforced, injection molding, improved impact strength Applications: automotive bumber-parts, tool-grips, bike-fenders, ski-shoe parts, suitcase-rollers |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.06 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction 1 | 1.5 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours 2 | 0.46 | -- | % | ISO 2577 |
| Flow direction 3 | 1.1 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours 4 | 0.38 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 80.0 | 35.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 1800 | 800 | MPa | ASTM D638 |
| 23°C | 1800 | 800 | MPa | ISO 527-2/1 |
| Tensile Strength (Yield, 23°C) | 45.0 | 35.0 | MPa | ASTM D638, ISO 527-2/50 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | -- | % | ASTM D638 |
| Yield, 23°C | 4.5 | 30 | % | ISO 527-2/50 |
| Fracture, 23°C | > 200 | > 200 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | ||||
| 23°C | 1600 | 752 | MPa | ASTM D790 |
| 23°C 6 | 1600 | 700 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 5.0% strain, 23°C | 55.2 | 31.0 | MPa | ASTM D790 |
| 23°C 7 | 60.0 | 30.0 | MPa | ISO 178/A |
| 3.5% strain, 23°C 8 | 55.0 | 25.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 9 | 7.0 | 9.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior (> 1.00 mm) | Passed | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Residual Moisture Content 10 | 0.030 - 0.12 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 85 | 120 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 650 | 650 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 650 | 920 | J/m | ASTM D256 |
| -30°C | 30 | 17 | kJ/m² | ISO 180/1A |
| 23°C | 70 | 100 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 125 | -- | J | ISO 6603-2 |
| 23°C | 120 | 125 | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, not annealed, 3.99mm | 90.0 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 90.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed, 3.99mm | 50.0 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 40.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 150 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (194°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 11357 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.5E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.6E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 36 | 36 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 50 Hz 11 | 3.30 | 9.60 | IEC 60250 | |
| 1 MHz | 3.10 | 3.50 | IEC 60250 | |
| 100 Hz | 3.30 | 11.0 | IEC 60250 | |
| 1 MHz | 3.00 | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.010 | 0.15 | IEC 60250 | |
| 23°C, 1 MHz | 0.010 | 0.060 | IEC 60250 | |
| Comparative Tracking Index (CTI) | -- | 600 | V | ASTM D3638 |
| Comparative Tracking Index | IEC 60112 | |||
| Solution a | 600 | -- | V | IEC 60112 |
| Solution B | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 12 | 21 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3; 260 °C / MT 80 °C; 500 bar |
| 2 . | Post-shrinkage: 150x105x3; 120 °C; 4 h |
| 3 . | 150x105x3; 260 °C / MT 80 °C; 500 bar |
| 4 . | Post-shrinkage: 150x105x3; 120 °C; 4 h |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Karl Fischer |
| 11 . | Tinfoil electrodes |
| 12 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech P704 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Tislamid® PA6 PA6 30 GFR | Tisan | Nylon 6 | Tislamid® PA6 |
| Trexprene® A80CI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| XYRON™ X552H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Fainplast PVC MPH 57 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |