| Message |
|---|
|
Glass-fibre reinforced phenolic moulding compound Very good electrical properties, good chemical resistance and mechanical properties This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 to 1.75 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 to 0.80 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.60 to 0.80 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Post Shrinkage 2 | 0.10 to 0.20 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 5000 to 7000 | MPa | ISO 527-2 |
| Tensile Stress (Injection Molded) | 50.0 to 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 7000 to 9000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 100 to 120 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.0 to 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Injection Molded) | 6.0 to 9.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/C |
| Thermal Conductivity | 0.40 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 12.0 10.0 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.60 to 0.80 | ||
| 1 MHz | 0.040 to 0.060 | ||
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index | > 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by Synres-Almoco) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| IPC PP 4800H | International Polymers Corporation | PP Homopolymer | IPC PP |
| LNP™ LUBRICOMP™ KFL23LH compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| Plasmer 7080B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| PENTAMID B natural (dryblend) | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| LNP™ THERMOCOMP™ QF007 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |