Lustran® SAN 51
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v1Gz8F_Lustran-SAN-51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran SAN 51 resin is an injection molding grade of transparent SAN (styrene acrylonitrile) thermoplastic. Lustran SAN 51 resin is the toughest grade with the best chemical resistance in the Lustran SAN product line. It has a large molding window and is easy to process. Lustran SAN 51 resin is available in natural (000000) color. Lustran SAN 51 resin is used in demanding applications requiring extra toughness and superior chemical resistance. Typical applications include industrial battery cases and disposable lighters. Lustran SAN 51 performs exceptionally well in applications that are subject to demanding environments. Finished products are resistant to heat deformation, scratching, and chemicals, such as acids, alkalies, and petroleum products. Common solvents, such as MEK and THF, can be used for bonding Lustran SAN 51. Parts molded out of Lustran SAN 51 resin also accept various methods of printing. As with any product, use of Lustran SAN 51 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Specific Volume | 0.930 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ASTM D638 |
| Tensile Strength (Break) | 76.0 | MPa | ASTM D638 |
| Flexural Modulus | 3600 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 131 | MPa | ASTM D790 |
| Deformation Under Load 1(50°C, 28 MPa) | 1.50 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 24 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 12.7mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 2 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.570 | ASTM D542 | |
| Haze (3200 µm) | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.0 - 88.0 | °C | |
| B | 71.0 - 77.0 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 175 - 185 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 205 - 215 | °C | |
| Nozzle Temperature | 205 - 215 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 40 to 80% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 24 hrs |
| 2 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6523 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Wellamid® XT1482-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Andur 9200 AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| DINALON® B1S25 M (Black) | Grupo Repol | Nylon 6 | DINALON® |
| GELOY™ XP4034 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |