Chemlon® MDT10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v0smqv_Chemlon-MDT10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MDT10 is a modified nylon 6 that offers ultra high impact strength coupled with good rigidity, with this impact resistance being retained at sub-zero temperatures. The excellent impact performance also means that it may be possible to use mouldings prior to any conditioning. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 42.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 140 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Flexural Stress 1 | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | No Break | ISO 179 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact | No Break | ISO 180 | |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 10 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.10 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | Internal method | |
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 250 - 280 | °C | |
| Middle Temperature | 250 - 280 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| Back pressure: LowInjection pressure: HighNo drying is necessary unless the materials has been exposed to air for longer than three hours. |
| Note Message | |
|---|---|
| 1 . | At conventional deflection |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUGUARD™ HPN469V2CSL | ACLO Compounders Inc. | PP Homopolymer | ACCUGUARD™ |
| LAMINEX® 2141 | Schwartz Technical Plastic | PF | LAMINEX® |
| Sylvin 83054-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SABIC® HDPE CLARENE 3H677 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| THERMOLAST® K TC7HFZ (Series: UV/HF/SF) | KRAIBURG TPE | TPE | THERMOLAST® K |