ENVIROPLAS® ENV42-NC740
| Category: | PEI+PC , Polyether Imide + PC |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v0aTTL_ENVIROPLAS-ENV42-NC740.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, 20% Fiberglass Reinforced, Flame Retardant, High Flow, Excellent Thermal Performance, High Mechanical Strength and Stiffness, RoHS Compliant NC470 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. The ENV42 Series Products Are Available With Mold Release and/or UV Stabilizer. Contact Enviroplas Regarding UL Recognized Versions Of This Product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 104 | MPa | ASTM D638 |
| Flexural Modulus | 9310 | MPa | ASTM D790 |
| Flexural Strength | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 187 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 5VA | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 321 to 332 | °C | |
| Middle Temperature | 327 to 343 | °C | |
| Front Temperature | 338 to 354 | °C | |
| Nozzle Temperature | 332 to 343 | °C | |
| Mold Temperature | 98.9 to 110 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502-A Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| Sindustris PP TE5105 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Clariant Nylon 6/6 PA-111G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| TECACOMP® PBT TC black 4207 | Ensinger GmbH | PBT | TECACOMP® |
| LEXAN™ SLX1432 resin | SABIC Innovative Plastics | PC | LEXAN™ |