Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ WF008 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v0ObHg_LNPTHERMOCOMPWF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WF008 is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound WF-1008 Product reorder name: WF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 12500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 128 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 11500 | MPa | ASTM D790 |
| Flexural Strength | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 750 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 211 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000-R01 | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| SCHULADUR® A1 GF 30 LW | A. Schulman Europe | PBT+PET | SCHULADUR® |
| Novamid® 1040J | DSM Engineering Plastics | Nylon 6 | Novamid® |
| Bergamid™ MD A70 G50 H NC | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Hostacom HKP 215D BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |