AXELERON™ CS K-3364 NT CPD
| Category: | HDPE , High Density Polyethylene Solid Insulation Compound |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AXELERON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v06PkD_AXELERON-CS-K-3364-NT-CPD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AXELERON™ CS K-3364 NT CPD is a high-molecular weight, high-density polyethylene insulation compound ("CPD") specifically formulated to provide excellent oxidative stability, toughness, and abrasion resistance. It provides superior long term aging performance, while providing excellent environmental and thermal stress-cracking resistance. In addition, AXELERON™ CS K-3364 NT CPD provides excellent processability for high-speed wire insulating extrusion processes. AXELERON™ CS K-3364 NT CPD provides good performance for telephone insulation applications, primarily cable designs for aerial environments. AXELERON™ CS K-3364 NT CPD is optimized to meet major international age testing standards and specifications for both solid and foam/skin insulation use. Specifications AXELERON™ CS K-3364 NT CPD meets the following raw material specifications:
Telephone wire insulated with AXELERON™ CS K-3364 NT CPD, using sound commercial extrusion practices, should meet the following cable specifications:
|
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100°C, 100% Igepal, F0) | > 48.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile strength retention- 48 hrs (100°C) | 90 | % | ASTM D638 |
| Elongation retention rate- 48 hrs (100°C) | 90 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat resistant stress crack- F0 | > 96 | hr | ASTM D2951 |
| Brittleness Temperature 1 | -76.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant 2(1 MHz) | 2.32 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 6.0E-5 | ASTM D1531 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 218 - 260 | °C |
| Extrusion instructions |
|---|
| AXELERON™ CS K-3364 NT CPD provides excellent surface finish and good output rates over a broad range of extrusion conditions. AXELERON™ CS K-3364 NT CPD is typically extruded at melt discharge temperatures ranging from 218-260°C (425-500°F) using conductor preheats ranging from 110-140°C (230-290°F). Specific extrusion conditions can be recommended only when the application, processing speed and processing equipment details are known. |
| Note Message | |
|---|---|
| 1 . | F0 |
| 2 . | After 14 days Water Immersion at 23°C (73°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 A2LG6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Tecomid® NA30 NL RM | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Star L PA66 15Y D52 | Eurostar Engineering Plastics | Nylon 66 | Star L |
| APEX® 2075-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Elastane™ 4762-86A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |