Niblend F17
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uzccDx_Niblend-F17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-ABS alloy reinforced with 17% glass fibre, of high thermic resistance for the injection moulding of items needing high hardness and dimensional stability even at high temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 50 | J/m | |
| 23°C, 3.20 mm | 70 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 4.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.050 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 SI 2 Z | RTP Company | PC | RTP |
| SUMIPEX® BF3 | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| Topolymer® 8229-P | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| GAPEX® RPP30EA20HB-BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Kingfa API-1508 | Kingfa | PP, Unspecified | Kingfa |