NEALID XG370
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uzOMrE_NEALID-XG370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID XG370 is a glass fibre reinforced polyamide alloy intended for Injection moulding. APPLICATIONS NEALID XG370 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. NEALID XG370 is available in both natural (NEALID XG370) and black (NEALID XG370-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10100 | 9250 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 132 | 117 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 8900 | 8250 | MPa | ISO 178 |
| Flexural Stress | 199 | 178 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 12 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 38 | 40 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 246 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+15 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 245 to 270 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 245 to 270 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANCOMP PP BN140 T5 | Polykemi AB | PP, Unspecified | SCANCOMP PP |
| Ultramid® B3WG6 GPX | BASF Corporation | Nylon 6 | Ultramid® |
| Flexalloy® 9100-45 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| ENGAGE™ 8402 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| TechnoDur PBT2 FR Natural (9984) | TechnoCompound GmbH | PBT | TechnoDur |