VENYL UG370
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uyupNM_VENYL-UG370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UG370 is a polyamide 66 glass fibre reinforced with medium viscosity intended for injection moulding, which offers a low coefficient of friction. APPLICATIONS VENYL UG370 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL UG370 offers better lubricated and a lower coefficient of friction. VENYL UG370 is available in both black/grey. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 to 0.80 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 to 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 175 to 200 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7750 to 8250 | MPa | ISO 178 |
| Flexural Stress | 230 to 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 to 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 to 35 | kJ/m² | ISO 179 |
| Notched Izod Impact | 90 to 95 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3980H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| PROFIL™ PPH3GF17-BK | Pier One Polymers, Inc. | PP Homopolymer | PROFIL™ |
| STYRON™ 668 | Americas Styrenics LLC | PS (GPPS) | STYRON™ |
| APEX® RE 9203 | Teknor Apex Company | PVC, Rigid | APEX® |
| Ferro Nylon RNY20LA | Ferro Corporation | Nylon 6 | Ferro Nylon |