Cereplast Hybrid Resins® 101
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Hybrid Resins® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uypiO6_Cereplast-Hybrid-Resins-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Hybrid Resins® are bio-based compounds containing a significant amount of renewable, ecologically sound sources such as starches from corn, tapioca, wheat and potatoes. Combined with a lower petroleum-based plastic content and renewable resources content, Cereplast Hybrid Resins® offer a significant carbon footprint reduction in the final product. Hybrid 101 is based on a high quality Polypropylene compounded on state-of-the-art mixing equipments using a proprietary formulation. Hybrid 101 offers a unique combination of mechanical properties, ease of processing, high aesthetic surface. Hybrid 101 has been designed to have an excellent balance between impact strength, rigidity and processability. Hybrid 101 can be processed on existing conventional electric and hydraulic reciprocating screw injection molding machines. Please see our processing guide for guidelines. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 965 | MPa | ASTM D638 |
| Tensile Strength (Break) | 17.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 689 | MPa | ASTM D790 |
| Flexural Strength | 21.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.9 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 71.1 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 171 to 182 | °C | |
| Middle Temperature | 177 to 193 | °C | |
| Front Temperature | 182 to 193 | °C | |
| Nozzle Temperature | 182 to 193 | °C | |
| Processing (Melt) Temp | 177 to 199 | °C | |
| Screw Speed | 50 to 100 | rpm | |
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 | ||
| Vent Depth | 0.051 to 0.064 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech C9704 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC | Sup-tech |
| Aaron AVPP C 200-2 | Aaron Industries Corp. | PP Copolymer | Aaron |
| Geon™ Vinyl Flexible R7661A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Iupilon® CLS3400 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| OLEFISTA™ QX0238E | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |