LNP™ STAT-LOY™ A3000T compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uyfnAK_LNPSTATLOYA3000Tcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat. Also known as: LNP* STAT-LOY* Compound A Product reorder name: A3000T |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.83 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.68 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1380 | MPa | ASTM D638 |
| -- | 1140 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 31.7 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2 |
| Fracture | 23.4 | MPa | ASTM D638 |
| Fracture | 24.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 39 | % | ASTM D638 |
| Fracture | 63 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1380 | MPa | ASTM D790 |
| -- | 1400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 41.4 | MPa | ASTM D790 |
| -- | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 80.6 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 3 | 81.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 86.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 67.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 182 - 193 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 204 - 216 | °C | |
| Processing (Melt) Temp | 199 - 210 | °C | |
| Mold Temperature | 10.0 - 26.7 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1370 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| CERTENE™ HHP-1244 | Muehlstein | HDPE | CERTENE™ |
| HydroThane™ 85A | CardioTech International, Inc. | PUR, Unspecified | HydroThane™ |
| Lumid® GP1000B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |
| CYCOLAC™ INP563 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |