NORYL™ FP5140HF resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uyM3Tn_NORYL-FP5140HF-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYLFP5140HF is an unfilled, injection moldable modified polyphenylene ether resin with an ISO306 Vicat B/120 of 100 deg C. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5mm with a specific density of 1.11g/cm3. NORYL FP5140 may be an excellent material for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/1.2 kg | 17.0 | cm³/10min | |
| 280°C/2.16 kg | 48.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.18 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2950 | MPa | ASTM D638 |
| -- | 2530 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 48.0 | MPa | |
| Break | 44.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 2.7 | % | |
| Break | 21 | % | |
| Flexural Modulus 2 | 2460 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.4 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ASTM D1525, ISO 306/B50 8 6 |
| -- | 100 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 250 to 285 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 40.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E195 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| DENILEN B 4010 CB WT | Vamp Tech | PP, Unspecified | DENILEN |
| INEOS PP N02J-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| Petrothene® NA373244 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 8950-90 White 1368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |