Garaflex™ G 7782-A4
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | AlphaGary |
| Trademark: | Garaflex™ G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uyK6GB_Garaflex-G-7782-A4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GARAFLEX G 7782-A4 IS A THERMOPLASTIC ELASTOMER INTENDED FOR FLEXIBLE CORD (SEO, SJEO). |
| General Information | |
|---|---|
| Uses |
|
| Wire Types |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 - 1.02 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 82 - 88 | ASTM D2240 | |
| Shaw A, 15 seconds | 78 - 84 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 19.0 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 600 | % | ASTM D412 |
| Tear Strength 1(0.762 mm) | 70.1 | kN/m | ASTM D624 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 2(136°C, 168 hr) | 0.0 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 3(136°C, 168 hr) | -5.0 | % | UL Unspecified |
| Change in Tensile Strength 4(60°C, 168 hr, in ASTM #2 Oil) | -10 | % | UL Unspecified |
| Change in Ultimate Elongation 5(60°C, 168 hr, in ASTM #2 Oil) | 0.0 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Deformation 6 | ASTM D2219 | ||
| 121°C, 889.0 µm | 5.5 | % | ASTM D2219 |
| 150°C, 889.0 µm | 8.9 | % | ASTM D2219 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 9.8E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (23°C, 1 MHz) | 1.0E-4 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 191 | °C | |
| Cylinder Zone 2 Temp. | 196 | °C | |
| Cylinder Zone 3 Temp. | 196 | °C | |
| Cylinder Zone 4 Temp. | 202 | °C | |
| Adapter Temperature | 204 | °C | |
| Melt Temperature | 210 - 232 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Screw Design: General Purpose Polyethylene Screw (C/R 2.5:1 3.5:1)Screen Pack: 40/80 or 40/100 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Thickness: 30 mil |
| 3 . | Thickness: 30 mil |
| 4 . | Thickness: 30 mil |
| 5 . | Thickness: 30 mil |
| 6 . | 1 hr, 2000 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 802 GB 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| UNISOFT ADHESION™ AD-65A-NT-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |
| ESENTTIA 08H85DB-P | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Huaxia Shenzhou DS603-B | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluoropolymer | Huaxia Shenzhou |
| LNP™ LUBRICOMP™ QCP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |