SABIC® HDPE P5510N
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uxofa9_SABIC-HDPE-P5510N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Provisional Data Sheet P5510N is a grade, which has a high density (class MRS 8 - PE 80) and a bimodal distribution of the molecular mass. An universal grade for pipe extrusion which, due to a keen combination of properties. It can be used for telecommunication, corrugated and spiral pipes. P5510N is a natural High Density Polyethylene (HDPE) resin specifcally designed for Pipe Extrusion. It provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.944 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 10 | g/10 min | |
| 190°C/5.0 kg | 0.43 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 850 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress (Yield, 2.00 mm, Compression Molded) | 22.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Yield, 2.00 mm, Compression Molded) | 10 | % | ISO 527-2/1BA/50 |
| Flexural Creep Modulus - 4 point, 1 min-value | 1.00 | GPa | DIN 19537-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | > 20 | min | EN 728 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 67.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1387 TFE 13 SI 2 | RTP Company | PPS | RTP |
| SABIC® PC PC4800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| HiFill® PA6 GF/B20 A3 BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ THERMOCOMP™ UFW49RSC compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |
| Sylvin 8260-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |