LNP STAT-KON RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound STATKON-RF-15 Product reorder name: RFD03 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.64 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 88.0 | MPa | ISO 527-2/5 |
| Fracture | 88.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.5 | % | ISO 527-2/5 |
| Fracture | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6600 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 256 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 240 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.6E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 3042 | SILON s.ro | LLDPE+EVA | TABOND |
| TOTAL Polypropylene PPC 3645 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Evolue™ SP1020 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| POLYfill PPH GF20005 PD2 UV | Polykemi AB | PP Homopolymer | POLYfill |
| Sylvin 6240-80 Pink 6278 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |