ULTEM™ HU2310 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uxWcnB_ULTEM-HU2310-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 7.6 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9240 | MPa | ASTM D638 |
| -- | 9500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 169 | MPa | ASTM D638 |
| Yield | 165 | MPa | ISO 527-2/5 |
| Break 3 | 159 | MPa | ASTM D638 |
| Break | 165 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9250 | MPa | ASTM D790 |
| -- 7 | 8500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 225 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 210 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 210 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 228 | °C | ASTM D1525 13 |
| -- | 213 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -20 to 150°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 1.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -20 to 150°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5563 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| RJM SA122-85 | RJM International, Inc. | PC+ABS | RJM |
| Tenite™ Propionate 380A4000015 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| BorSafe™ HE3496-LS | Borealis AG | HDPE | BorSafe™ |
| Hifax 7334 XEP | LyondellBasell Industries | TPO (POE) | Hifax |