NORYL™ PX0888 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uxVDlH_NORYLPX0888resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled, non-FR. Higher heat resistance than N110 (BOZ) and px0844 (USA). For automotive interiors. 250F (121C) DTUL. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 2360 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 130 | J/m | ASTM D256 |
| 23°C | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 129 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 128 | °C | ASTM D648 |
| CLTE - Flow (0 to 100°C) | 7.4E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 249 - 299 | °C | |
| Middle Temperature | 260 - 304 | °C | |
| Front Temperature | 271 - 310 | °C | |
| Nozzle Temperature | 282 - 310 | °C | |
| Processing (Melt) Temp | 282 - 310 | °C | |
| Mold Temperature | 77 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9501 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| Hostacom PF072-2C | LyondellBasell Industries | PP Homopolymer | Hostacom |
| KMI PE KM-7417BDNP | KMI Group, Inc. | LLDPE | KMI PE |
| Sylvin 8707-84 Brown 7382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ICORENE® 3560 | ICO Polymers NA, A Division of A. Schulman | LLDPE | ICORENE® |