LG ABS HI121
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uxGtiN_LG-ABS-HI121.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS HI121 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG ABS HI121 are:
Typical application of LG ABS HI121: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Dimensional Stability | 0.0 | % | ASTM D1042 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2080 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 45.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 3.20 mm) | 72.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 130 | J/m | |
| -30°C, 6.40 mm | 130 | J/m | |
| 23°C, 3.20 mm | 340 | J/m | |
| 23°C, 6.40 mm | 310 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 91.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 6 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 100 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 100 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 100 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 27 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3735 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| BITONER® BT-2110 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| ALCUDIA® LDPE PE-033 | REPSOL | LDPE | ALCUDIA® LDPE |
| Geon™ Vinyl Rigid Extrusion LR840 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hiprolon® 11 ECN Blue H8L | Arkema | Nylon 1012 | Hiprolon® |