ISPLEN® PM 370 AE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uwmGpo_ISPLEN-PM-370-AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer, 30% mineral fillers reinforced and high melt flow rate. ISPLEN PM370 AE gives a good compromise between stiffness and impact strength, a low warpage and shrinkage behaviour. This product is high heat stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.50 to 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 34.0 | MPa | |
| Break | 33.5 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.0 | % | |
| Break | 4.0 | % | |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 1.4 | kJ/m² | |
| 0°C | 1.5 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 12 | kJ/m² | |
| 0°C | 14 | kJ/m² | |
| 23°C | 23 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 22 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A120 |
| -- | 108 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120G45 | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| DENILEN B 4010 CB WT | Vamp Tech | PP, Unspecified | DENILEN |
| Electrafil® PC C BK | Techmer Engineered Solutions | PC | Electrafil® |
| Kumho EPS EPOR 30 I | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Lion Idemitsu Composites PPS C-140MG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |