LNP™ LUBRICOMP™ UCL36ASP compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uwfXck_LNP-LUBRICOMP-UCL36ASP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* UCL36ASP is a compound based on Polyphtalamide resin containing Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound UCL-4036 A Product reorder name: UCL36ASP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.050 to 0.10 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.050 to 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 256 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19900 | MPa | ISO 178 |
| Flexural Stress | 340 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.33 | ASTM D3702 Modified | |
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 270 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.0E-6 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 310 | Wacker Chemie AG | Silicone | POWERSIL® |
| Sindustris ABS LHG284 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sindustris PP GP3210A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Geon™ Vinyl Flexible R148AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Lion Idemitsu Composites PPS K521A2 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |