IROGRAN® A 95 H 4678
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uvr7lQ_IROGRAN-A-95-H-4678.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 95 H 4678 is a thermoplastic polyester-polyurethane for injection moulding applications. Additional characteristics of the product are short cycle times, good melt flows and easy demolding. PERFORMANCE FEATURES
APPLICATIONS For the production of technical parts, conveyor rollerswheels and rollers, suitcase wheels and rollers, bearing shells. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.23 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (210°C/10.0 kg) | 78.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (Injection Molded) | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, Injection Molded | 95 | ||
| Shore D, Injection Molded | 45 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 30 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | ASTM D412, DIN 53504 | ||
| 100% Strain | 13.0 | MPa | |
| 300% Strain | 26.0 | MPa | |
| Tensile Strength 4 | |||
| Break | 50.0 | MPa | ASTM D412 |
| Break | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 5(Break) | 500 | % | ASTM D412, DIN 53504 |
| Tear Strength 6 | 120 | kN/m | ASTM D624, ISO 34-1 |
| Compression Set 7 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 40 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 145 to 200 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 195 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 175 to 195 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 190 | °C | |
| Cylinder Zone 2 Temp. | 165 to 190 | °C | |
| Cylinder Zone 3 Temp. | 165 to 190 | °C | |
| Cylinder Zone 4 Temp. | 165 to 190 | °C | |
| Cylinder Zone 5 Temp. | 165 to 190 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LB02019 - B | Premier Polymers, LLC. | LLDPE | Premier |
| SAXAMID™ 226F10 | SAX Polymers | Nylon 66 | SAXAMID™ |
| Zytel® 70G33HS1L BK031 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| ESPRENE EPDM 512F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Latilub 67-10STE21 G/20 | LATI S.p.A. | Nylon 66 | Latilub |