Network Polymers PP 30 0100 GF40
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uvbNEu_Network-Polymers-PP-30-0100-GF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Network Polymers PP 30 0100 GF40 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 40% glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 0.318 mm, Injection Molded) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break, 23°C, 3.18 mm, Injection Molded) | 93.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.18 mm, Injection Molded) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent 4(23°C, 3.18 mm, Injection Molded) | 7580 | MPa | ASTM D790 |
| Flexural Strength 5(23°C, 3.18 mm, Injection Molded) | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm, Injection Molded | 163 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm, Injection Molded | 154 | °C | |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 |
| Melting Temperature | 163 | °C | ASTM D785 |
| CLTE - Flow | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (@1.5mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 40 | % | ASTM D2584 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene RCC220-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| CET® 240 | Resirene, S.A. de C.V. | Acrylic (SMMA) | CET® |
| Iupital® F10-01 F10-02 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Isocor™ CU145SI | Shakespeare Monofilaments and Specialty Polymers | Nylon 66/6 | Isocor™ |
| Optix® CA-82 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |