NOVADURAN® 5010GN6-15T
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | NOVADURAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uuIg0V_NOVADURAN-5010GN6-15T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVADURAN® 5010GN6-15T is a Polybutylene Terephthalate (PBT) material filled with 15% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of NOVADURAN® 5010GN6-15T are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 2.00 mm | 1.5 | % | |
| Flow : 2.00 mm | 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.070 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5900 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 53 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 216 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Melting Temperature | 224 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 50°C | 3.0E-5 | cm/cm/°C | |
| Flow : -30 to 120°C | 4.0E-5 | cm/cm/°C | |
| Flow : 50 to 120°C | 4.0E-5 | cm/cm/°C | |
| Transverse : -30 to 50°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -30 to 120°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 50 to 120°C | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.017 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.710 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 235 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 255 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic THVP 2030GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| InnoClear™ OC-5080 | Innovative Polymers, Inc. | TSU | InnoClear™ |
| SIBUR Synthetic Rubber SBR-1706 Grade D | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |
| Sylvin 916VO Grey 9256 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ WFL369 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |