LNP™ STAT-KON™ EX03319C compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | utwqAX_LNP-STAT-KON-EX03319C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON EX03319C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding application. A unique feature of this material is its low non-volatile residue (NVR). This compound is manufactured using LNP CCS Technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.050 to 0.15 | % | |
| Across Flow : 24 hr | 0.30 to 0.45 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 17000 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 224 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 11600 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 233 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 7(23°C) | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 350 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 205 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 to 5.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+3 to 5.0E+6 | ohms·cm | ASTM D257 |
| Static Decay 8 | 0.1 | sec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 330 to 380 | °C | |
| Middle Temperature | 340 to 380 | °C | |
| Front Temperature | 345 to 380 | °C | |
| Nozzle Temperature | 345 to 380 | °C | |
| Processing (Melt) Temp | 350 to 380 | °C | |
| Mold Temperature | 135 to 165 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PEI-G10 | Polymer Resources Ltd. | PEI | PRL |
| Diablend 6500 | DTR S.r.l. (Develop Thermoplastic Resins) | PC+ABS | Diablend |
| ELASTOSIL® 4000 | Wacker Chemie AG | Silicone | ELASTOSIL® |
| Geon™ Vinyl Flexible B7D00 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 2990-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |