Multiuse Leostomer® LJ-3190N
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Riken Technos Corp. |
| Trademark: | Multiuse Leostomer® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | utFSWS_Multiuse-Leostomer-LJ-3190N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Multiuse Leostomer®LJ-3190N is a thermoplastic polyurethane elastomer product,. It can be processed by injection molding and is available in North America or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 86 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 4.80 | MPa | ISO 37 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 920 | % | ISO 37 |
| Tear Strength | 67 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| -- | 57 | % | ISO 815 |
| 70°C, 22 hr | 50 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (50°C, 24 hr, in IRM 902 oil) | -11 | % | ISO 1817 |
| Change in Tensile Strain at Break (50°C, 24 hr, in IRM 902 oil) | 9.0 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ISO 974 |
| Additional Information |
|---|
| The values listed above are tested in accordance with JIS K test methods.Injection speedFast0Rebound Resilience: 38%Die Temperature: 20 to 40°CInjection Pressure: LowMaintained Pressure: LowBack Pressure: Low |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RxLOY™ FFS-NPP00NP03NA | Ferro Corporation | PP Alloy | RxLOY™ |
| Sanren Y200L (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| TABOREN PH 41 C 40 | SILON s.ro | PP Homopolymer | TABOREN |
| Fainplast PVC FK 90/13 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Koattro KT AR05 | LyondellBasell Industries | Plastomer | Koattro |