Lupoy® SC1004A
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uso3t3_Lupoy-SC1004A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, High Toughness, Chemical resistance, High Impact (at Low Temperature) Application Mobile Phone Housing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 55.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 130 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2060 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5 | ASTM D256 | ||
| -30°C | 55 | J/m | |
| 23°C | 70 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 130 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Minimum Moisture Content | 0.020 | % | |
| Rear Temperature | 275 to 290 | °C | |
| Middle Temperature | 285 to 305 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 285 to 305 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 3.2 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAFMER™ A-0585S | Mitsui Chemicals America, Inc. | PAO | TAFMER™ |
| Thanelene® TPU S80A15 PRTA010 TP305 MSP | Petropol Industry and Trade of Polymers LTDA | TPU-Polyester | Thanelene® TPU |
| Topilene® J340 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| CompaMid® PA 6 GF 25 | DimeLika Plast GmbH | Nylon 6 | CompaMid® |
| Flontech® FT-COND2-3 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |