Edistir® N 2560
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | urTSuS_Edistir-N-2560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High molecular weight general purpose polystyrene with good mechanical strength and good thermal resistance. It is recommended for in—line forming of disposable packaging, for sheet extrusion in blend with conventional or clear high impact PS and for injection moulding of complex items requiring good toughness and improved elasticity. Designation: Thermoplastics ISO 1622-PS,G,095-03 Applications Suitable for thermoformed food packaging articles as drink and dairy cups, plates, trays and for injection moulded cd boxes, domestic appliances, stationery, cutlery, housewares. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.8 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Stress 1 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 1.6 | kJ/m² | ISO 180/1A |
| 23°C | 1.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/A50 |
| -- | 91.0 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 2.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastics ISO 1622-PS,G,095-03 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C |
| Injection instructions |
|---|
| Predrying normally not required |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PP FR2 NAT | RTP Company | PP, Unspecified | RTP |
| Smooth-Cast® ONYX® Fast | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| UNISOFT TPE™ ST-75A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Fainplast PVC PM 8220 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KEBATER® PBT A0230 | BARLOG plastics GmbH | ABS+PBT | KEBATER® |