Order Products : sales@su-jiao.com
ARLEN™ G335
| Category: | Nylon 6T , Polyamide 6T |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | ARLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ur7k9q_ARLENG335.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARLEN™G335 is a polyamide 6T (nylon 6T) material, which contains a 35% glass fiber reinforced material. This product is available in North America,. ARLEN™The main characteristics of G335 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.47 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00mm | 0.20 | -- | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.50 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.30 | -- | % | ASTM D570 |
| 100°C, 24 hr | 1.7 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 200 | 180 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | 10000 | MPa | ASTM D790 |
| Flexural Strength | 340 | 310 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 100 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 280 | -- | °C | ASTM D648 |
| Glass Transition Temperature | 140 | -- | °C | DSC |
| Melting Temperature | 300 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 28 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Hopper Temperature | 50 - 90 | °C | |
| Rear Temperature | 315 - 330 | °C | |
| Middle Temperature | 320 - 335 | °C | |
| Front Temperature | 325 - 340 | °C | |
| Nozzle Temperature | 325 - 340 | °C | |
| Mold Temperature | 90 - 140 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 150 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Medium Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound PHC25-20 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| SLOVALEN® PH 76 T 20 FRD 5 000/1M | Plastcom | PP, Unspecified | SLOVALEN® |
| SURPASS® FPs117-D | NOVA Chemicals | LLDPE | SURPASS® |
| Hifax CB 1128 A/1 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| POCAN® AF 4130 000000 | LANXESS GmbH | PBT+ASA | POCAN® |