Durethan® AKV 35 CX H2.0 900876
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uqGQuN_.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 35 % glass fibers, injection molding, heat aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 290°C, 2.00mm 1 | 0.90 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.070 | % | ISO 294-4 |
| Flow direction : 290°C, 2.00mm 3 | 0.30 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.070 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 197 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10900 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 296 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.2 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA 66, GHR, 12-110, GF35 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.020 - 0.070 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 58 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 240 | °C | ISO 75-2/A |
| Melting Temperature 8 | 260 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PH-88 | CHI MEI CORPORATION | PS (HIPS) | POLYREX® |
| RTV-2 XT-426 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Geon™ Vinyl Wire & Cable W780L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Lupox® GP2306FC | LG Chem Ltd. | PBT | Lupox® |
| ISOPAK® 569M | Great Eastern Resins Industrial Co., Ltd. (GRECO) | ABS | ISOPAK® |