DURANEX® 3116
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURANEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uqFHiq_DURANEX-3116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Retardant, Standard, UL Approved Regrind 50% Inclusive, GF7.5% reinforced, Standard |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 91.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2 |
| Flexural Modulus | 4710 | MPa | ISO 178 |
| Flexural Stress | 144 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.1 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 201 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 6.0E-5 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 9.0E-5 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | EF2001/ED3002 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Holding Pressure | 60.0 - 100 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Cooling Time: Plasticization time + alpha or time without sticking in mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3030 JI6L | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Yanshan PE 7000F | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| Borlink™ LE0504 | Borealis AG | PE, Unspecified | Borlink™ |
| ExxonMobil™ LDPE LD 101BA Wire & Cable | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Karina GREEN COLOR CONCENTRATE 40/14-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |