AKROTEK® PEEK CF 40 9 black (5182)
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | upt4xg_AKROTEK-PEEK-CF-40-9-black-5182-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PEEK CF 40 9 black (5182) is a 40% carbon fibre reinforced process improved polyetheretherketone with high flexural strength and good sliding properties Applications are mainly elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength and high stiffness in a temperature environment above 150°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.44 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 31500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 235 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 30000 | MPa | ISO 178 |
| Flexural Stress 2 | 345 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 1.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 36 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 280 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 260 | °C | ISO 75-2/C |
| Melting Temperature 4 | 342 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALECCA K-100 | Denka Company Limited | ABS | MALECCA |
| EvoSource™ ABS 4535 70/05 | MBA Polymers | ABS | EvoSource™ |
| FLEXITEQ™ F65A560 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Ebalta AH 100 / SR | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| LNP™ STAT-KON™ SX90398 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ STAT-KON™ |