Innothane® IE-65D
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | upfQFi_Innothane-IE-65D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-65D is a tough, impact resistant elastomer formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.06 | g/cm³ | |
| Cured | 1.08 | g/cm³ | |
| Base Resin | 1.09 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 241 | MPa | ASTM D790 |
| Flexural Strength | 13.1 | MPa | ASTM D790 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 20 Mix Ratio by Weight: 20 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 120 to 240 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Exotherm - 200g mass | 57 | °C |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 2.0 | Pa·s | |
| 25°C 3 | 3.0 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 10 to 14 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 45 to 55 | ASTM D2240 | |
| Tensile Strength | 16.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 210 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 180°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L MAT-1 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| Reon 60-11 | Reliance Industries Limited | PVC Homopolymer | Reon |
| 3M™ Dyneon™ Fluoroplastic PFA 6502UHPZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| Biocycle 18BC-1 | Biocycle | Biodeg Polymers | Biocycle |
| Isocor™ 6105 | Shakespeare Monofilaments and Specialty Polymers | Nylon 610 | Isocor™ |