Duron PPE/PA 820
| Category: | Nylon+PPE , Polyamide + PPE |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | Duron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | up7uGH_Duron-PPE-PA-820.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duron PPE/PA 820 is a 20% glass reinforced polyamide that is reinforced with a modified polyphenylene ether polymer. This combination provides improved dimensional stability and heat resistance compared to conventional nylon. It is lubricated which improves mold release and surface finish. Duron PA provides outstanding processability and chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.40 to 0.60 | % | |
| Across Flow : 3.18 mm | 0.70 to 0.80 | % | |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 7.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5960 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 194 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 254 | °C | |
| 1.8 MPa, Unannealed | 232 | °C | |
| Melting Temperature | 249 | °C | |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 UV | RTP Company | Nylon 66 | RTP |
| Starflex GM1210BE | LyondellBasell Industries | mLLDPE | Starflex |
| Ultramid® A3HG5 | BASF Corporation | Nylon 66 | Ultramid® |
| Nycal鈩?1820RMC40 Bk-1 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| LNP™ THERMOCOMP™ EC006PXQ compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |