PENTAMID A GV30 H MOS ungefärbt
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uosUzZ_PENTAMID-A-GV30-H-MOS-ungef-rbt.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, 30% glass fiber reinforced, modified with MoS2 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.75 | -- | % | ISO 294-4 |
| Flow direction | 0.45 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.1 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 250 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 175 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.3 | 3.9 | % | ISO 527-2 |
| Flexural Modulus | 9000 | -- | MPa | ISO 178 |
| Flexural Stress | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 25 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | -- | IEC 60250 | |
| Comparative Tracking Index | 350 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA66, MHRS, 14-100 N, GF30+X1The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA66, MHRS, 14-100 N, GF30+X1 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.090 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 270 - 295 | °C | |
| Middle Temperature | 285 - 300 | °C | |
| Front Temperature | 285 - 295 | °C | |
| Processing (Melt) Temp | 290 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 78.0 | MPa | |
| Holding Pressure | 46.8 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Semitron® CMP XL20 | Quadrant Engineering Plastic Products | PAI | Quadrant EPP |
| ACRYPET® IR H30 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| ALFATER XL® A80I 4FC0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Halene P R103 | Haldia Petrochemicals Ltd. | PP Homopolymer | Halene P |
| LEXAN™ HPH4704 resin | SABIC Innovative Plastics Asia Pacific | PPC | LEXAN™ |