Zytel® MT409AHS NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uok64z_ZytelMT409AHSNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.7 | -- | % | ISO 294-4 |
| Flow | 1.5 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.3 | -- | % | ISO 62 |
| Saturated, 23°C, 2.00mm | 4.9 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 61.0 | 43.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | 28 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2200 | 1000 | MPa | ISO 178 |
| Flexural Stress 1 | 75.0 | 53.0 | MPa | ISO 178 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Elongation - MD (Yield) | 4.4 | -- | % | ISO 527-3 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 13 | -- | kJ/m² | ISO 179/1eA |
| -30°C | 13 | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 21 | 40 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 13 | 11 | kJ/m² | ISO 180/1A |
| -30°C | 15 | 15 | kJ/m² | ISO 180/1A |
| 23°C | 18 | 29 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 2 | 80.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 3 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 3.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 23 | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.60 | 6.60 | IEC 60250 | |
| 1 MHz | 3.40 | 3.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.18 | IEC 60250 | |
| 1 MHz | 0.012 | 0.044 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | 29 | -- | mm/min | ISO 3795 |
| Flame Rating | ||||
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 0.8 mm | HB | -- | IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 | |
| Atomization- G-value (condensate) | 1.0E-4 | -- | g | ISO 6452 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2730 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.14 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 10.0 | -- | µgC/g | VDA 277 |
| Odor | 4.00 | -- | VDA 270 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 0.930 | -- | g/cm³ | |
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | Calculated |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| 4 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1203-28 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Sylvin 9714-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VINIKA® CD50EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Loyblend® TA-1101 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| SQUARE® LSR2034-65BS | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |