| Unreinforced, Heat Stabilized, Polyamide 612 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 3.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.3 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 115 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 62.0 | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.4 | 19 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2100 | 1450 | MPa | ISO 178 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Elongation - MD (Yield) | 4.4 | -- | % | ISO 527-3 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 4.0 | kJ/m² | |
| 23°C | 4.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 4.0 | 6.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 135 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.2E-4 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.7E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.8E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.60 | 5.30 | ||
| 1 MHz | 3.20 | 3.40 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.014 | 0.10 | ||
| 1 MHz | 0.016 | 0.040 | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.860 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers HDPE 50 0149 | Network Polymers, Inc. | EHMWPE | Network Polymers HDPE |
| AVP™ GYY01CP | SABIC Innovative Plastics | Nylon 66 | AVP™ |
| K-Bin Rigid PVC KBD-5030T-9 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |
| LUVOCOM® 1301-8456 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| ALCOM® LD2 PC 1000 14050 GY1118-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LD2 PC |