RTP ESD A 1480 N
| Category: | PESU , Polyethersulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uo4uHL_RTP-ESD-A-1480-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- ESD 1480 Series is a polyethersulfone resin with carbon fiber added for electrical conductivity. These products have excellent static dissipation characteristics and are non-sloughing. ESD A 1480 is static dissipati |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5860 | MPa | ASTM D638 |
| Tensile Strength | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 207 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| CLTE - Flow | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 4mil/in.Tensile Elongation, ASTM D638: 3-4%Volume Resistivity, ASTM D257: 10E3 -10E9 ohm-cmSurface Resistivity, ASTM D257: 10E6 -10E12 ohm/sqStatic Decay, FTMS-4046.1, Mil B-81705C: <2.0 seconds |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 316 - 399 | °C | |
| Middle Temperature | 316 - 399 | °C | |
| Front Temperature | 316 - 399 | °C | |
| Mold Temperature | 37.8 - 177 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HIPREN® EM 1502 T | HIP-PetroHemija | SBR, Emulsion | HIPREN® |
| Lucene™ LC760 | LG Chem Ltd. | TPO (POE) | Lucene™ |
| Sumiliteresin® PR-1040 AI | SBHPP | Phenolic | Sumiliteresin® |
| OTECH PVC OW138 - Power Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Latamid 12 H 90FE03 | LATI S.p.A. | Nylon 12 | Latamid |