Reblend® B4070 NATURALE
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Reblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | undIQG_Reblend-B4070-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS/PA blend, very high impact strenght |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 42.0 | MPa | |
| Break | 35.0 | MPa | |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 70 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 96.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 108 | °C | ISO 306 |
| Peak Melting Temperature | 220 | °C | ASTM D3417 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 912 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Nivionplast® A R356G NAT | SO.F.TER. SPA | Nylon 66 | Nivionplast® A |
| CompaDur® 125 GF 15 black (042) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| DURANEX® SF3300 | Polyplastics Co., Ltd. | PBT | DURANEX® |
| PENTAMID A GK30 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |