Zytel® HTN FR52G30NH NC010
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | unbMAl_Zytel-HTN-FR52G30NH-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.44 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9000 | 10000 | MPa | ISO 178 |
| Flexural Stress | 230 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 8.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 35 | kJ/m² | |
| 23°C | 45 | 40 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 283 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 90.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 36 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.400 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| Oxygen Index | 37 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 703 | RTP Company | HDPE | RTP |
| AEI SX409:CM401 | AEI Compounds Limited | LDPE | AEI |
| Avalon 88 | Greene, Tweed & Co. | PTFE | Avalon |
| K-PU 7775 | Technovinyl Polymers India Ltd. | TPU, Unspecified | K-PU |
| Plaslube® PA6/6 AF10 HS L | Techmer Engineered Solutions | Nylon 66 | Plaslube® |