Makropol® PC B3 MF FD CLRA010 PC319
| Category: | PC , Polycarbonate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Makropol® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | unD8V6_Makropol-PC-B3-MF-FD-CLRA010-PC319.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate transparent, medium viscosity, FDA - food contact quality, good hydrolysis resistance. Indicated for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.50 | cm³/10min | ASTM D1238 |
| Molding Shrinkage - Across Flow | 0.60 to 0.80 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2400 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus 3 | 2350 | MPa | ASTM D790 |
| Flexural Strength 4 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (Area) | ASTM D256 | ||
| -30°C | 12.0 | kJ/m² | |
| 23°C | 85.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 137 | °C | |
| 1.8 MPa, Unannealed | 125 | °C | |
| Vicat Softening Temperature | 144 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 32 | kV/mm | ASTM D149 |
| Relative Permittivity | 3.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 930 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 85.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 GR15 NL HS | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Yuyao PBT 3066G30 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| EPIMIX PBT GFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| HIVOREX 2700J | Lotte Chemical Corporation | HDPE | HIVOREX |
| LCA® T-85 Type | UniPlas, Inc. | PC+ABS | LCA® |