| GLAMIDE® T-402 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 19 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 to 0.40 | -- | % | |
| 3.00 mm | 0.40 to 0.70 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.3 | -- | % | |
| Equilibrium, 65% RH | 2.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 245 | 220 | MPa | |
| Yield, 23°C | 170 | 105 | MPa | |
| Yield, 80°C | 100 | 70.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 3.6 | 5.6 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 10800 | 9200 | MPa | |
| 23°C | 8500 | 5000 | MPa | |
| 80°C | 4500 | 3400 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 305 | 290 | MPa | |
| Yield, 23°C | 260 | 130 | MPa | |
| Yield, 80°C | 150 | 100 | MPa | |
| Compressive Strength (23°C) | 155 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 80 | 85 | J/m | |
| 23°C | 120 | 200 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 217 | -- | °C | |
| 1.8 MPa, Unannealed | 205 | -- | °C | |
| CLTE - Flow | 2.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 23 | 17 | kV/mm | ASTM D149 |
| Arc Resistance | 100 | 90.0 | sec | ASTM D495 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 to 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E590PUOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Atlac 711-05AS | Reichhold Chemicals, Inc. | Polyester, TS | Atlac |
| Crastin® S650FR BK851 | DuPont Performance Polymers | PBT | Crastin® |
| KOCETAL® WR303 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| ICORENE® 9402 | ICO Polymers EMEA, A Division of A. Schulman | TPE | ICORENE® |